Chinese liquid concrete sealing and curing agent Concrete reinforcing agent
SV-LLI lithium concrete sealing hardener
1. Overview
Lithium-based concrete sealing curing agent SV-LLI is a nano-lithium based waterborne inorganic concrete sealing curing agent, formulated by applying special technology. Through strong permeability and chemical components in concrete and cement floor chemical reaction, in the ground 4-8 mm three-dimensional space to form an overall network distribution and curing treatment, so as to compact concrete, in the overall surface strength of concrete strength, wear resistance, impermeability, dust, anti-slip and anti-aging performance reflects excellent quality, prolong the service life of concrete.
2. Technical indicators
|
Serial number
|
Inspection items
|
The standard requires
JC/T2158-2021
|
Test results
|
| 1 |
Appearance |
Colorless, transparent homogeneous liquid |
Colorless, transparent homogeneous liquid |
| 2 |
Solid content |
Explicit value±2% |
31% |
| 3 |
pH |
≥10.0 |
11.5 |
| 4 |
Viscosity (23°C) |
1.0mPa·s—10.0mPa·s |
1.6mPa·s |
| 5 |
Abrasion resistance (AR2)
|
≤0.20mm |
0.06mm |
| 6 |
Surface hardness |
≤4.5mm |
4.3mm |
| 7 |
24 surface water absorption |
≤5.0mm |
2.5mm |
3. Scope of application: concrete floor, terrazzo floor, emery floor, cement floor and other hard floors.
4. Dilution ratio: ordinary ground: 1:1-2 diluted with water. (Recommendation)
Abrasion-resistant/dense surface: 1:3-4 diluted with water. (Recommendation)
5. Recommended dosage: ordinary ground: 3-4 m2/kg (original solution)
Abrasion-resistant/dense surface: 8-10 m2/kg (stock solution)
6. Curing time: more than 8h
7. Quality level: qualified
8. Packaging and storage
30kg, 250kg, 1200kg plastic drum; Store in a cool, ventilated and dry place.